Indium antimonide

The intermetallic compound was first reported by Liu and Peretti in 1951, who gave its homogeneity range, structure type, and lattice constant.^[5] Polycrystalline ingots of InSb were prepared by Heinrich Welker in 1952, although they were not very pure by today's semiconductor standards. Welker was interested in systematically studying the semiconducting properties of the III-V compounds. He noted how InSb appeared to have a small direct band gap and a very high electron mobility.^[6] InSb crystals have been grown by slow cooling from liquid melt at least since 1954.^[7]

In 2018, a research team at Delft University of Technology claimed that indium antimonide nanowires showed potential application in creating Majorana zero mode quasiparticles for use in quantum computing; Microsoft opened a laboratory at the university to further this research, however Delft later retracted the paper.^[8][9]

InSb has the appearance of dark-grey silvery metal pieces or powder with vitreous lustre. When subjected to temperatures over 500 °C, it melts and decomposes, liberating antimony and antimony oxide vapors.

The crystal structure is zincblende with a 0.648 nm lattice constant.^[10]

 

InSb is a narrow direct band gap semiconductor with an energy band gap of 0.17 eV at 300 K and 0.23 eV at 80 K.^[10]

Undoped InSb possesses the largest ambient-temperature electron mobility of 78000 cm²/(V⋅s),^[11] electron drift velocity, and ballistic length (up to 0.7 μm at 300 K)^[10] of any known semiconductor, except for carbon nanotubes.

Indium antimonide photodiode detectors are photovoltaic, generating electric current when subjected to infrared radiation. InSb's internal quantum efficiency is effectively 100% but is a function of the thickness particularly for near bandedge photons.^[12] Like all narrow bandgap materials InSb detectors require periodic recalibrations, increasing the complexity of the imaging system. This added complexity is worthwhile where extreme sensitivity is required, e.g. in long-range military thermal imaging systems. InSb detectors also require cooling, as they have to operate at cryogenic temperatures (typically 80 K). Large arrays (up to 2048×2048 pixels) are available.^[13] HgCdTe and PtSi are materials with similar use.

A layer of indium antimonide sandwiched between layers of aluminium indium antimonide can act as a quantum well. In such a heterostructure InSb/AlInSb has recently been shown to exhibit a robust quantum Hall effect.^[14] This approach is studied in order to construct very fast transistors.^[15] Bipolar transistors operating at frequencies up to 85 GHz were constructed from indium antimonide in the late 1990s; field-effect transistors operating at over 200 GHz have been reported more recently (Intel/QinetiQ).^{[citation needed]} Some models suggest that terahertz frequencies are achievable with this material. Indium antimonide semiconductor devices are also capable of operating with voltages under 0.5 V, reducing their power requirements.^{[citation needed]}

InSb can be grown by solidifying a melt from the liquid state (Czochralski process), or epitaxially by liquid phase epitaxy, hot wall epitaxy or molecular beam epitaxy. It can also be grown from organometallic compounds by MOVPE.^{[citation needed]}

• Thermal image detectors using photodiodes or photoelectromagnetic detectors^{[citation needed]}
• Magnetic field sensors using magnetoresistance or the Hall effect^{[citation needed]}
• Fast transistors (in terms of dynamic switching). This is due to the high carrier mobility of InSb^{[citation needed]}
• In some of the detectors of the Infrared Array Camera on the Spitzer Space Telescope^{[citation needed]}

• Haynes, William M., ed. (2016). CRC Handbook of Chemistry and Physics (97th ed.). CRC Press. ISBN 9781498754293.

• National Compound Semiconductor Roadmap at the Office of Naval Research
• Material safety data sheet Archived 2016-03-03 at the Wayback Machine at University of Texas at Dallas